تحفيز نشاط المحفز الضوئي لأكسيد السيلينيوم متناهي الصغر باستخدام البلاتينيوم
Enhanced Photocatalytic Activity of ZrO(2)-SiO(2) Nanoparticles by Platinum Doping
 
الموضوع : علوم البيئة 
لغة الوثيقة : الانجليزية 
المستخلص : ZrO(2)-SiO(2) mixed oxides were prepared via the sol-gel method. Photo-assisted deposition was utilized for doping the prepared mixed oxide with 0.1, 0.2, 0.3, and 0.4 wt% of Pt. XRD spectra showed that doping did not result in the incorporation of Pt within the crystal structure of the material. UV-reflectance spectrometry showed that the band gap of ZrO(2)-SiO(2) decreased from 3.04 eV to 2.48 eV with 0.4 wt% Pt doping. The results show a specific surface area increase of 20%. Enhanced photocatalysis of Pt/ZrO(2)-SiO(2) was successfully tested on photo degradation of cyanide under illumination of visible light. 100% conversion was achieved within 20 min with 0.3 wt% of Pt doped ZrO(2)-SiO(2). 
ردمد : 1110-662X 
اسم الدورية : INTERNATIONAL JOURNAL OF PHOTOENERGY 
المجلد : 1 
العدد : 1 
سنة النشر : 1434 هـ
2013 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, June 3, 2013 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
محمد قاضيKadi, Mohammad W. باحث  
R. M. MohamedMohamed, R. M. باحث rmmohammed@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 35604.pdf pdfEnhanced Photocatalytic Activity of ZrO(2)-SiO(2) Nanoparticles by Platinum Doping

الرجوع إلى صفحة الأبحاث